Cam Elyaf Kumaş İle Desteklenmiş Köşe Birleştirmelerde Eğilme Moment Direnci

Anahtar Kelimeler:

Çekme ve basma direnci, Epoxy, PVAc, PU, Ahşap bisküvi

The Bending Moment Resistance of Corner Joints Reinforced with Glass Fiber Polymer

Aim of study: This study aimed to determine the effects of glass fiber reinforced polymer (GFRP) and adhesives type on the diagonal compression and tensile strength in L-type corner joints connected by a wood biscuit. Material and Methods: Medium density fiberboard coated with melamine plate (MDFlam), wood biscuit with a size number of 20 (dimension: 56 × 23 × 4 mm) as the joining member, GFRP for strengthening purposes, and polyvinyl acetate (PVAc-D4), polyurethane (PU-D4), and epoxy glues as adhesives were used. The diagonal compression and tension tests were carried out under static load according to ASTM-D1037 standards. Main results: Results indicated that using GFRP significantly increased the diagonal compression and tensile strength of L-type corner joints connected by a wood biscuit. Highlights: It is recommended to use the combination of GFRP and epoxy adhesive in the corner joints to have better compression and tensile strength in furniture.

Keywords:

Adhesive Tensile and Compression, Epoxy, PVAc, PU, Wood biscuit,

PDF

___

Akgül, T. 2007. Strengthening of wood and joints with fiber-reinforced polymers. M. Sc. Thesis, Institute of Natural Sciences, Sakarya University, Sakarya, 13-42.
Anshari, B., Kitamori, A., Jung, K., Komatsu, K., Guan, Z. 2011. Experimental study on structural behavior of glulam beams pre-stressed by compressed wood. Wood research Journal 2(1), 54-61.
Bal, C. Özyurt, H. 2015. Some technological properties OF laminated veneer lumber reinforced WITH woven glass fiber. KSU. Journal of Engineering Sciences, 18(1), 2015, 9-16.
Claisse, P.A., and Davis, T.J. 1998. High performance jointing systems for timber. Construction and Building Materials. 12, 415-425 Çelikel, Ü., 2006. The Effects of wood louse tongue (biscuit joint) on the strength of corner joints in case furniture. Master Thesis, G.Ü. Institute of Natural Sciences, Ankara, 48s.
Demirel, E., 2008. The Effects of Different Types of Glue and Material Used on the Corner Joining of Box Type Furniture Constructions. Master Thesis, Z.K.Ü. Institute of Science, Bartın.
Karaman, A., Güven, Ş., Yeşil, H., Yıldırım, MN, (2017). Determination of the diagonal tensile force and pressure force in furniture corner assemblies prepared by using different glues. SDU Journal of Technical Sciences, 7 (2), 26-36.
Mıstak, O., (2013). Determination of mechanical properties of lamina wood materials obtained with scots pine and different fiber (FRP) fabrics. M.Sc. Thesis, Karabük University Institute of Science, Karabük, 49-66.
Nikolaos, P., Thanasis, T. (1992). FRP-Reinforced Wood as Structural Material. Journal of Materials in Civil Engineering 4(3), 300-317.
Osmannezhad, S., Faezipour, M., Ebrahimi, G. (2014). Effects of GFRP on bending strength of glulam made of poplar (Populus deltoids) and beech (Fagus orientalis). Construction and Building Materials, 51, 34-39.
Plevris, N., Triantafillou, T.C. (1992). FRP-reinforced wood as structural material. J. Mat. Civ. Engrg. ASCE, 4(3), 300-317.
Rowell, R. (2005). Handbook of Wood Chemistry and Wood Composites. CRC Press, ISBN 0-8493-1588-3, New York.
Smardzevski, J. (2002). Technological heterogeneity of adhesive bonds in wood joints. Wood Science and Technology. 36 (3), 213–227. Yerlikaya, N., (2014). Effects of glass–fiber composite, dowel, and minifix fasteners on the failure load of corner joints in particleboard case-type furniture. Materials and Design, 39, 63-71.
Zhang, J.L., Erdil, Y.Z., Eckelman, C.A. (2002). Lateral Holding Strength of Dowel Joints Constructed of Plywood and Oriented Strandboard. Forest Product Journal, 52 (7/8), 83 – 89.
Zhang, J.L., Eckelman, C.A. (1993). The bending moment resistance of single-dowel corner joints in case construction. Forest Product Journal, 43 (6), 19 – 24